NBRClick Here +
NBR has a wide range of applications. It is used extensively in making gaskets, o-rings and oil resistant seals. Additionally it is also used for rubber linings of industrial vessels.
| Grade | Bound Acrylonitrile(%) | Mooney Viscosity | ML 1+4, (1000C) product Stain | Polymerization | Temperature Specific Gravity |
|---|---|---|---|---|---|
| KNB 35L | 34 | 41 | NST | Cold | 0.98 |
SBRClick Here +
SBR is primarily used in the footwear and Tire industry. It also used in hoses, conveyor belts and other mechanical goods. It is usually used in conjunction with PBR and natural rubber at the time of mixing
| Grade | Type | Bound Styrene | Mooney Viscosity ML 1+4 (1000 C) | Product Stain | Extender oil Type/Parts |
Emulsifier | Coagulant |
|---|---|---|---|---|---|---|---|
| 1502 | Cold | 23.5 | 52 | NST | - | RA/FA | Salt-Acid |
EPDMClick Here +
EPDM is used to make moulded automobile components, cable insulations, tire tubes and construction roofing sheets.
| Type | Mooney Viscosity (ML 1+4, 125 0 C) |
ENB Content (Wt. %) |
Ethylene Content (Wt. %) |
Extender Oil (PHR) | Product Form (1) | Features | Applications |
|---|---|---|---|---|---|---|---|
| KEP435 | 33 | 2.3 | 57 | - | B | Low mooney viscosity & slow vulcanization speed, execellent heat & ozone resistance, optimum scorch safety in blending with IIR | Automobile tire tubes, waterproof sheet, heat resistant belt |
| KEP210 | 23 | 5.7 | 65 | - | B | Low mooney viscosity & high vulcanization speed, good processability & high extrusion speed | Wires, cables, automobile parts, window seals, sponge |
| KEP240 | 42 | 4.5 | 57 | - | B | Medium vulcanization speed & good rocessability, good balance of vulcanization speed and physical properties | Various types of industrial parts, automobile parts and injection molding goods etc. |
| KEP270 | 71 | 4.5 | 57 | - | B | High mooney viscosity & medium vulcanization speed, high filler loading | Heat resistant hose, washing machine hose, window seals, various types of automobile parts. |
| KEP330 | 28 | 7.9 | 57 | - | B | Low mooney viscosity & excellent processability, high vulcanization speed, blend with diene rubber | Tire coverstrip, white sidewall, window seals, gaskets, packings, sponges |
| KEP350 | 56 | 7.9 | 57 | - | B | High mooney viscosity & excellent processability, high vulcanization speed, blend with diene rubber | Tire coverstrip, white sidewall, window seals, gaskets, packings, sponges |
PBRClick Here +
PBR is extensively used in the tire industry. It is also used in footwear soles and mechanical rubber products.
KHSClick Here +
KHS 68 finds extensive use in the footwear industry for shoe heels and soles. It is also used in moulded car parts and rubber hoses.
| Grade | Total styrene Content(%) | Mooney Viscosity ML5+4 (1000 C) | Product Stain | Emulsifier | Coagulant | Appearance |
|---|---|---|---|---|---|---|
| KHS 68 | 68 | 61 | NST | RA/FA | Salt-Acid | Popcorn |
SILICON RUBBERClick Here +
General Purpose.
Extrusion Grades
High Elongation Grades
High Tear-40n/mm tear grades
High Temp-up to 300 Deg. intermediate
High Transparency
FDA Grades
| Product Series | Grade | Specific Gravity ISO 2781 | Appearance | Post cure | Shore A Hardness ASTM D 2240 | Tensile Strength (Mpa) ISO 37 | Elongation break (%) ISO 37 | Tear Strength (KN/m) ASTM D 624A | Compression set(%) (22h/177 C/ 25%) | Rebound resilience(%) ISO 4662 | Advantages | Applications |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
|
HCR 1900 Good mechanical properties general products |
HCR 1920L | 1.07 | Transcluent | - | 21 | 7.3 | 987 | 14 * 2 | 46 * 1 | 50 |
Good transparent and anti-yellowing Good process ability, not sticky to rolls, easy to demold excellent mechanical properties Good heat resistance Short vulcanizing time Good anti-creep haredening ability |
Kitchenware Automotive technical parts Electronic appliances Wire & Cable Office automation Various extruded profiles |
| HCR 1930L | 1.08 | Transcluent | - | 31 | 8.2 | 821 | 12 * 2 | 43 * 1 | 59 | |||
| HCR 1940L | 1.12 | Transcluent | - | 41 | 8.8 | 658 | 15 * 2 | 27 * 1 | 59 | |||
| HCR 1950L | 1.15 | Transcluent | - | 49 | 9.1 | 525 | 16 * 2 | 24 * 1 | 54 | |||
| HCR 1960L | 1.18 | Transcluent | - | 61 | 8.8 | 429 | 17 * 2 | 19 * 1 | 50 | |||
| HCR 1970L | 1.21 | Transcluent | - | 70 | 8.1 | 361 | 18 * 2 | 19 * 1 | 44 | |||
| HCR 1980L | 1.23 | Transcluent | - | 80 | 7.8 | 218 | 14 * 2 | 17 * 1 | 46 |
NEOPRENEClick Here +
NEOPRENE is used in wire and cable jackets, automotive parts and general industrial parts.